108 RED CLAY W/GROG
Cone 6-10
A high fire clay with medium grog and sand for surface texture and minimal warping and cracking. Designed for sculpture, slab or coil building. Suggested bisque temperature C/04. Shrinkage:10.5% at C/6,12% at C/10. Absorption: 5.5% at C/6, 3% at C/10.
![](https://www.queencityclay.com/wp-content/uploads/2016/03/108c6.jpg)
108
![](https://www.queencityclay.com/wp-content/uploads/2016/03/108c10.jpg)
108
![](https://www.queencityclay.com/wp-content/uploads/2016/03/108c10R.jpg)
108
119 STONEWARE CLAY
Cone 6-10
Contains coarse silica sand. Good for both salt and wood firings. Suggested bisque temperature C/04. Shrinkage: 10.5% at C/6, 12% at C/10. Absorption: 3.5% at C/6, 2.5% at C/10.
![](https://www.queencityclay.com/wp-content/uploads/2016/03/119c6.jpg)
119
![](https://www.queencityclay.com/wp-content/uploads/2016/03/119c10.jpg)
119
![](https://www.queencityclay.com/wp-content/uploads/2016/03/119c10R.jpg)
119
153 STONEWARE CLAY
Cone 6-10
A soft warm beige in oxidation - a rich gray brown in reduction. Responds well to all techniques. Excellent for production potters and classroom use. Suggested bisque temperature C/04. Shrinkage: 11.5% at C/6, 13% at C/10. Absorption: 5% at C/6, 2% at C/10
![](https://www.queencityclay.com/wp-content/uploads/2016/03/153c6.jpg)
153
![](https://www.queencityclay.com/wp-content/uploads/2016/03/153c10.jpg)
153
![](https://www.queencityclay.com/wp-content/uploads/2016/03/153c10R.jpg)
153
181 WHITE STONEWARE
Cone 6-10
A very smooth white stoneware body. Contains no fire clay. Suggested bisque temperature C/04. Shrinkage: 13% at C/6, 13.9% at C/10. Absorption: 2.8% at C/6, 1.7% at C/10.
![](https://www.queencityclay.com/wp-content/uploads/2016/03/181c6.jpg)
181
![](https://www.queencityclay.com/wp-content/uploads/2016/03/181c10.jpg)
181
![](https://www.queencityclay.com/wp-content/uploads/2016/03/181c10R.jpg)
181
182 WHITE STONEWARE
Cone 6-10
Near white plastic stoneware body. Good for use with bright glazes. Suggested bisque temperature C/04. Available with and without fine grog. Suggested bisque temperature C/04. Shrinkage: 11% at C/8, 12% at C/10. Absorption: 3% at C/8, 2.1% at C/10.
![](https://www.queencityclay.com/wp-content/uploads/2016/03/182c6.jpg)
182
![](https://www.queencityclay.com/wp-content/uploads/2016/03/182c10.jpg)
182
![](https://www.queencityclay.com/wp-content/uploads/2016/03/182c10R.jpg)
182
259 STONEWARE CLAY
Cone 6-10
Formulated to be similar to 153, but with richer color tones. Shrinkage: 12.25% at C/6, 13% at C/10. Suggested bisque temperature C/04. Absorption: 4% at C/6, .85% at C/10.
![](https://www.queencityclay.com/wp-content/uploads/2016/03/259c6.jpg)
259
![](https://www.queencityclay.com/wp-content/uploads/2016/03/259c10.jpg)
259
![](https://www.queencityclay.com/wp-content/uploads/2016/03/259c10R.jpg)
259
306 BROWN FIRING CLAY
Cone 6-10
Smooth throwing body. Orange-brown in reduction. Muted orange to C/4 oxidation. Gray at C/10 oxidation. Suggested bisque temperature C/04. Shrinkage: 11.5% at C/6, 13% at C/10. Absorption: 3.5% at C/6, 1% at C/10.
![](https://www.queencityclay.com/wp-content/uploads/2016/03/306c6.jpg)
306
![](https://www.queencityclay.com/wp-content/uploads/2016/03/306c10.jpg)
306
![](https://www.queencityclay.com/wp-content/uploads/2016/03/306c10R.jpg)